拉伸中應力硬化的本質：剪切與拉伸的區別 |
|
|
|
| 資料類型： |
PDF文件
|
| 關鍵詞： |
strain hardening 應力硬化 線性高分子 支化高分子 拉伸 |
| 資料大小： |
1647k |
| 所屬學科： |
高分子物理 |
| 來源： |
來源網絡 |
| 簡介： |
|
討論拉伸中應力硬化出現的根本原因。
Thisworkstudiestheoriginofthesocalled"strainhardening"observedwhencomparingthetransientstressresponseofentangledmeltstouniaxialextensionwiththattosimpleshear.Strainhardeningoccurswhenthetransientextensionalviscositymeasuredfromastartupuniaxialextensionoffiniteratedeviatesupwardfromthezero-ratetransientviscosity.OurtheoreticalanalysisshowsthatpolymermeltswouldalwaysexhibitstrainhardeningatsufficienthighHenckyratesbecausetheentanglementnetworkcanbeeffectivelystrengthenedduringextensionandcanonlybeweakenedduringshearforlinearchains.Thekinematicdifferencebetweensimpleshearanduniaxialextensionhastwoeffects:(a)Theforceresultingfromthestartupdeformationismeasuredfromanincreasinglyshrinkingareainuniaxialextensioninsteadofaconstantareaasinsimpleshear;and(b)thetendencyoftheentanglementnetworktoyield,i.e.,toundergochaindisentanglementispartiallysuppressedduringstartupextensionathighHenckyrates.Inshort,thephenomenonofstrainhardeningreflectstherealitythatentangledmeltsarenotfluidsbuttemporarysolidsandthattheconventionaldescriptionoftheiruniaxialextensionintermsoftheCauchystresscontainsageometriccondensationfactor. |
|
| 上傳人： |
stude
|
| 上傳時間： |
2014-04-26 10:55:56 |
| 下載次數： |
16 |
| 消耗積分： |
2
|
| 立即下載： |
|
|
| 友情提示：下載后對該資源進行評論，即可獎勵2分。 |
|
| 報告錯誤： |
1.下載無效
2. 資料明顯無價值
3. 資料重復存在 |
| |
|
|
| 你還沒有登錄，無法發表評論，請首先 |
 |
| 免責聲明：本站部分資源由網友推薦，來自互聯網，版權屬于原版權人，如果不慎侵犯到您的權利，敬請告知，我們會在第一時間撤除。本站中各網友的評論只代表其個人觀點，不代表本站同意其觀點。 |
|
|
|
|