Preparation of Primary Amine-Based Block Copolymer Vesicles by Direct Dissolution in Water and Subsequent Stabilization by Sol-Gel Chemistry
作者:Jianzhong Du* and Steve Armes
關鍵字:polymer vesicles, self-assembly
論文來源:期刊
具體來源:Langmuir 2008, 24, 13710-13716.
發表時間:2008年

A new amphiphilic biocompatible diblock copolymer, poly(ε-caprolactone)-block-poly(2-aminoethyl methacrylate), PCL-b-PAMA, was synthesized in three steps by (i) ring-opening polymerization of ε-caprolactone, (ii) end-group modification by esterification, and (iii) atom transfer radical polymerization (ATRP) of 2-aminoethyl methacrylate hydrochloride (AMA) in its hydrochloride salt form. This copolymer forms block copolymer vesicles with the hydrophobic PCL block forming the vesicle membrane. Unusually, these vesicles are easily prepared by direct dissolution in water without using organic co-solvents, pH adjustment, or even stirring. These vesicles can be stabilized by aqueous sol−gel chemistry using tetramethyl orthosilicate (TMOS) as the silica precursor. It is well-known that cationic polymers can catalyze silica formation, but in this particular case, it seems that the TMOS precursor is solubilized within the hydrophobic PCL membrane. Thus, the neutral membrane actually directs silica formation, rather than the cationic PAMA chains. The final vesicle morphology and the silica content depend on the silicification conditions. Provided that the TMOS/AMA molar ratio does not exceed 10:1, silicification is solely confined within the PCL membrane. At higher ratios, silica nanoparticles (5−12 nm) are also observed on the outer surface of the silicified vesicles. However, these nanoparticles appear to be only weakly adsorbed, since they can be easily removed by dialysis. The mean hydrodynamic diameter of the silicified vesicles varies from 175 to 205 nm with solution pH due to (de)protonation of the externally expressed PAMA chains. Calcination of the silicified vesicles at 800 °C leads to the formation of hollow silica particles. 1H NMR, transmission electron microscopy (TEM), dynamic light scattering (DLS), aqueous electrophoresis, and thermogravimetric analysis (TGA) were employed to characterize the vesicles, both before and after silicification.

http://pubs.acs.org/doi/abs/10.1021/la8025123?prevSearch=%255Bauthor%253A%2Bjianzhong%2Bdu%255D&searchHistoryKey=