Multifunctional Ti3C2Tx-(Fe3O4/polyimide)
composite films with Janus structure for outstanding electromagnetic
interference shielding and superior visual thermal management. Nano Research,
2022, 10.1007/s12274-022-4358-7. 2020IF=8.897.（1區(qū)材料科學(xué)Top期刊，中國(guó)科技期刊卓越行動(dòng)計(jì)劃-領(lǐng)軍類期刊項(xiàng)目，2021中國(guó)最具國(guó)際影響力學(xué)術(shù)期刊）
https://doi.org/10.1007/s12274-022-4358-7
Abstract
Flexible multifunctional polymer-based
electromagnetic interference (EMI) shielding composite films have important
application values in the fields of 5G communication technology, wearable
electronic devices and artificial intelligence. In this work, Fe3O4/polyamic
acid (PAA) nanofiber films are prepared by in-situ polymerization and
electrospinning technology, and Ti3C2Tx nanosheets are deposited on the surface of the Fe3O4/PAA
nanofiber films via vacuum-assisted filtration. Then, Janus Ti3C2Tx-(Fe3O4/polyimide
(PI)) composite films are obtained by thermal imidization. The two sides of the
Janus films exhibit completely different properties. The Fe3O4/PI
side has excellent hydrophobicity and insulation property, and the Ti3C2Tx side has terrific hydrophilicity and conductivity. When the mass fraction of Ti3C2Tx is 80 wt%, the Janus Ti3C2Tx-(Fe3O4/PI)
composite film has excellent EMI shielding performances and mechanical
properties, with EMI shielding effectiveness, tensile strength and Young’s
modulus reaching 66 dB, 114.5 MPa and 5.8 GPa, respectively. At the same time,
electromagnetic waves show different absorption shielding effectiveness (SEA)
when incident from two sides of the Janus films. When the electromagnetic waves
are incident from the Fe3O4/PI side, the SEA of the Janus film is 58 dB, much higher than that when the electromagnetic
waves are incident from the Ti3C2Tx side (39
dB). In addition, the Ti3C2Tx side of the Janus
Ti3C2Tx-(Fe3O4/PI)
composite films also have excellent electrothermal and photothermal conversion performances.
When the applied voltage is 4 V, the stable surface temperature reaches 108oC;
when it is irradiated by simulated sunlight with power density of 200 mW/cm2,
the stable surface temperature reaches 95oC.
柔性多功能聚合物基電磁干擾（EMI）屏蔽復(fù)合膜在5G通信技術(shù)、可穿戴電子設(shè)備和人工智能等領(lǐng)域具有重要的應(yīng)用價(jià)值。本文通過(guò)“原位聚合-靜電紡絲”法制備四氧化三鐵/聚酰胺酸（Fe3O4/PAA）納米纖維膜，借助真空輔助抽濾在Fe3O4/PAA納米纖維膜表面沉積Ti3C2Tx納米片，再經(jīng)熱亞胺化制備具有Janus結(jié)構(gòu)的Ti3C2Tx-（Fe3O4/聚酰亞胺（PI））復(fù)合膜。該復(fù)合膜兩側(cè)表現(xiàn)出截然不同的性質(zhì)，Fe3O4/PI側(cè)具有優(yōu)異的疏水性和絕緣性，而Ti3C2Tx側(cè)具有出色的親水性和導(dǎo)電性。當(dāng)Ti3C2Tx質(zhì)量分?jǐn)?shù)為80 wt%時(shí)，Ti3C2Tx-（Fe3O4/PI）復(fù)合膜兼具優(yōu)異的屏蔽性能和力學(xué)性能，EMI屏蔽效能達(dá)到66 dB、拉伸強(qiáng)度和楊氏模量分別達(dá)到114.5 MPa和5.8 GPa。同時(shí)，電磁波從Janus結(jié)構(gòu)復(fù)合膜兩側(cè)入射時(shí)表現(xiàn)出不同的EMI吸收屏蔽效能（SEA）。當(dāng)電磁波從Fe3O4/PI側(cè)入射時(shí)，復(fù)合膜的SEA為58 dB，遠(yuǎn)高于從Ti3C2Tx側(cè)入射時(shí)的SEA（39 dB）。此外，Ti3C2Tx-（Fe3O4/PI）復(fù)合膜的Ti3C2Tx側(cè)還具有優(yōu)異的電熱和光熱轉(zhuǎn)化性能。當(dāng)施加4 V電壓時(shí)，其表面穩(wěn)定溫度達(dá)到108oC；當(dāng)受到功率密度為200 mW/cm2模擬太陽(yáng)光照射時(shí)，表面穩(wěn)定溫度達(dá)到95oC。
本文亮點(diǎn)
1. 通過(guò)原位聚合-靜電紡絲、真空輔助抽濾及熱亞胺化工藝制備的具有Janus結(jié)構(gòu)的多功能Ti3C2Tx-（Fe3O4/PI）復(fù)合膜兩側(cè)表現(xiàn)出截然不同的性質(zhì)，Fe3O4/PI側(cè)具有優(yōu)異的疏水性和絕緣性，而Ti3C2Tx側(cè)具有出色的親水性和導(dǎo)電性。
2. 當(dāng)Ti3C2Tx質(zhì)量分?jǐn)?shù)為80 wt%時(shí)，Ti3C2Tx-（Fe3O4/PI）復(fù)合膜的EMI屏蔽效能高達(dá)66 dB。電磁波從Janus結(jié)構(gòu)復(fù)合膜的兩側(cè)入射時(shí)表現(xiàn)出不同的SEA。當(dāng)電磁波從復(fù)合膜的Fe3O4/PI側(cè)入射時(shí)，復(fù)合膜的SEA為58 dB，高于從Ti3C2Tx側(cè)入射時(shí)的SEA（39 dB）。
3. Ti3C2Tx-（Fe3O4/PI）復(fù)合膜的Ti3C2Tx側(cè)還具有優(yōu)異的電熱和光熱轉(zhuǎn)化性能。當(dāng)施加4 V電壓時(shí)，其表面穩(wěn)定溫度達(dá)到108oC；當(dāng)受到功率密度為200 mW/cm2的模擬太陽(yáng)光照射時(shí)，表面穩(wěn)定溫度達(dá)到95oC。