Composites Part B:對(duì)比研究空心和實(shí)心玻璃微珠對(duì)聚二甲基硅氧烷/多壁碳納米管復(fù)合材料的電磁屏蔽性能增強(qiáng)
全文鏈接:https://doi.org/10.1016/j.compositesb.2019.107378
Herein, solid and hollow glass microspheres (SGM and HGM) were added into polydimethylsiloxane/multiwalled carbon nanotube (PDMS/MWCNT) composites to induce multiple interfaces. The electromagnetic interference (EMI) shielding of the PDMS/MWCNT composites was expectedly enhanced by the multiple reflection and/or scattering at the interfaces between GM and PDMS/MWCNT phase. The EMI shielding effectiveness (SE) of the PDMS/MWCNT composites with 3.0 vol% MWCNT fillers increased from ~40 to ~52 dB and ~46 dB by the addition of 30 vol% SGM and HGM, respectively. The high specific SE value was found in the composites with HGM due to the low density of the samples with HGM. The effect of the diameter and the content of SGM, the content of MWCNT, and the sample thickness on EMI SE of the PDMS/MWCNT/SGM
composites were investigated in this work. The high-performance EMI SE were achieved in the composites by balancing the thickness of conductive layers and the amount of multiple reflection and/or scattering interfaces.