Interfacial entanglement between glassy polymers investigated by nanofractography with high-resolution scanning electron microscopy.
來源:廖永貴副教授個人網站 發布日期:2009-09-22
作者:Shin Horiuchi, Ayumi Nakagawa, Yonggui Liao, Toshiaki Ougizawa.
關鍵字:Macromolecules 2008, 41(21): 8063-8071.
論文來源:期刊

Fracture surfaces created during the interfacial failure of weak interfaces between glassy polymers were investigated with high-resolution scanning electron microscopy (HR-SEM). As reported in an earlier communication (Macromol. Rapid Commun. 2007, 28, 915-921), we found that interfacial failures between immiscible polymers produced large number of nanosized fibrils on the fracture surfaces. In order to investigate the mechanism of such ultra small structure formation in the crack propagation process, welding experiments of monodispersed polystyrenes with different molecular weights were employed by the asymmetric double cantilever beam (ADCB) test. The “nano-fibrils” were produced during the fractures of the interfaces between polystyrenes with the molecular weight higher than 2000, of which thickness was comparable to the entanglement spacing. It was found that the “nano-fibrous” formation bearing in the crack propagation reflected the local entanglement structures formed at narrow interfaces comparable to the entanglement spacing.

Copyright © 2005 Polymer.cn All rights reserved
中國聚合物網 版權所有
經營性網站備案信息

京公網安備11010502032929號

工商備案公示信息

京ICP證050801號

京ICP備12003651號

主站蜘蛛池模板: 巴林左旗| 漠河县| 饶平县| 白沙| 东山县| 扎鲁特旗| 禄丰县| 巴中市| 涡阳县| 金平| 长岛县| 佳木斯市| 民勤县| 辰溪县| 邯郸市| 鄂州市| 观塘区| 丹寨县| 左云县| 乾安县| 天峻县| 莆田市| 静乐县| 榆林市| 南溪县| 错那县| 两当县| 柞水县| 乐平市| 磴口县| 抚远县| 娱乐| 高阳县| 迁西县| 获嘉县| 临邑县| 咸丰县| 岳池县| 庆城县| 宁乡县| 玉田县|