Facile synthesis of hyperbranched and star-shaped polymers by RAFT polymerization based on a polymerizable trithiocarbonate
來源:趙優(yōu)良教授個人網站 發(fā)布日期:2012-01-29
作者:Chengbo Zhang, Yuan Zhou, Qiang Liu, Shixian Li, Sébastien Perrier, Youliang Zhao*
關鍵字:hyperbranched polymer, star polymer, RAFT polymerization, self-condensing vinyl polymerization
論文來源:期刊
具體來源:Macromolecules, 2011, 44, 2034-2049
發(fā)表時間:2011年

pubs.acs.org/doi/abs/10.1021/ma1024736

Facile synthesis of hyperbranched and star polymers on the basis of S-(4-vinyl)benzyl S’-propyltrithiocarbonate (VBPT) was described. RAFT copolymerization of VBPT with vinyl monomers such as methyl methacrylates (MMA), styrene (St), methyl acrylate (MA) and tert-butyl acrylate (tBA) afforded hyperbranched copolymers with variable branch length and degree of branching. Hyperbranched copolymers obtained at a low feed ratio of vinyl monomers to VBPT usually possessed repeat units per branch higher than the expected values due to the presence of VBPT unit with pendant trithiocarbonate group and side reactions resulting in partial loss of CTA functionality. RAFT copolymerization at various feed ratios afforded poly(VBPT-co-MA) branched copolymers with weight-average CTA functionality up to 107 or more, which were further used to generate star PSt and PtBA with adjustable molecular weight and variable polydispersity (1.12 < PDI < 1.88). The approach based on two successive RAFT processes is general and versatile to synthesize multiarm star polymers with controllable arm length. The resultant polymers were characterized by 1H NMR, GPC-MALLS, DSC and TGA. The intrinsic viscosities of branched and star-shaped polymers were lower than those of their linear analogues with same molecular weights; both Mark-Houwink-Sakurada exponent and contractor factor of branched copolymers were observed to increase with decreasing degree of branching, thus confirming a branching nature. The single glass transition temperature in DSC traces indicated branched copolymers obtained at various feed ratios had good compatibility.

 

 

Copyright © 2005 Polymer.cn All rights reserved
中國聚合物網 版權所有
經營性網站備案信息

京公網安備11010502032929號

工商備案公示信息

京ICP證050801號

京ICP備12003651號

主站蜘蛛池模板: 开鲁县| 偏关县| 错那县| 密云县| 宁都县| 瑞金市| 玉溪市| 玛曲县| 江安县| 宜章县| 利津县| 林甸县| 汾阳市| 定边县| 日照市| 大冶市| 南开区| 宣恩县| 宝山区| 综艺| 凭祥市| 乌拉特后旗| 龙门县| 安吉县| 察隅县| 固阳县| 乾安县| 万州区| 滦南县| 项城市| 巴里| 都安| 丽水市| 长垣县| 高陵县| 沧源| 东台市| 霞浦县| 长乐市| 宜都市| 绥棱县|