Cubic MnFe2O4 particles decorated reduced graphene oxide with excellent microwave absorption properties
作者：Gengyuan Zhang, Ruiwen Shu*, Yan Xie, Haitao Xia, Ying Gan, Jianjun Shi, Jie H
關鍵字：Reduced graphene oxide, Manganese ferrite, Carbon materials, Nanocomposites, Microwave absorption
論文來源：期刊
具體來源：Materials Letters
發(fā)表時間：2018年
Herein, we have fabricated the reduced graphene oxide/manganese ferrite (RGO/MnFe2O4) hybrid composites by a facile one-pot hydrothermal method. The obtained MnFe2O4 particles exhibited the uniquely cubic morphology with an average particle size of 100.6 nm, which were uniformly attached to the surface of RGO sheets. Results demonstrated that both the ratio of RGO to MnFe2O4 and filling ratio had notable effects on the microwave absorption performance of the as-prepared hybrid composites. Moreover, the hybrid composites showed the characteristics of thin thickness, broad bandwidth and strong absorption. Significantly, the hybrid composite with a filling ratio of 70 wt% (S2) exhibited the best microwave absorption performance, i.e. the minimum reflection loss reached 47.5 dB and effective absorption bandwidth (less than 10 dB) was 5.2 GHz for a thickness of only 1.7 mm. Therefore, the RGO/MnFe2O4 hybrid composites could be potential candidates for application in microwave absorption.