Acceleration or Retardation to Crystallization if Liquid-Liquid Phase Separation Occurs: Studies on a Polyolefin Blend by SAXS/WAXD, DSC and TEM.
作者:Yanhua Niu, Zhigang Wang*, Carlos Avila Orta, Donghua Xu, Howard Wang, Katsumi Shimizu, Benjamin
關鍵字:Crystallization, Liquideliquid phase separation, Polyolefin blend
論文來源:期刊
具體來源:Polymer 2007, 48, 6668-6680.
發表時間:2007年

Blends of statistical copolymers containing ethylene/hexene (PEH) and ethylene/butene (PEB) exhibited the behavior of upper critical solution temperature (UCST). The interplay between the early and intermediate stage liquideliquid phase separation (LLPS) and crystallization of the PEH/PEB 50/50 blend was studied by time-resolved simultaneous small-angle X-ray scattering (SAXS) and wide-angle X-ray diffraction (WAXD) techniques. Samples were treated by two different quench procedures: in single quench, the sample was directly quenched from 160 C to isothermal crystallization temperature of 114 C; while in double quench, the sample was firstly quenched to 130 C for 20 min annealing, where LLPS occurred, and then to 114 C. It was found that in the early stage of crystallization, the integrated values of Iq2 and crystallinity, Xc, in the double quench procedure were consistently higher than those in the single quench procedure, which could be attributed to accelerated nucleation induced by enhanced concentration fluctuations and interfacial tension. In the late stage of crystallization, some morphological parameters were found to crossover and then reverse, which could be explained by retardation of lamellar growth due to phase separation formed during the double quench procedure. This phenomenon was also confirmed by DSC measurements in blends of different compositions at varying isothermal crystallization temperatures. The crystal lamellar thickness determined by SAXS showed a good agreement with TEM observation. Results indicated that the early stage LLPS in the PEH/PEB blend prior to crystallization indeed dictated the resulting lamellar structures, including the average size of lamellar stack and the stack distribution. There seemed to be little variation of lamellar thickness and long period between the two quenching procedures (i.e., single quench versus double quench).


主站蜘蛛池模板: 望江县| 武冈市| 台中市| 扎鲁特旗| 勃利县| 武安市| 天长市| 宜良县| 都安| 舟曲县| 佛坪县| 手游| 延寿县| 万载县| 临桂县| 永胜县| 扎囊县| 宜川县| 巴林右旗| 民县| 宜丰县| 惠州市| 湟源县| 渝中区| 吉隆县| 大足县| 灌南县| 辽宁省| 峡江县| 浮山县| 阿瓦提县| 安图县| 桂平市| 招远市| 永胜县| 华阴市| 济南市| 曲阳县| 武定县| 华安县| 库尔勒市|