Electrospun poly(3-hydroxybutyrate-co-3-hydroxy- valerate)/cellulose reinforced nanofibrous membranes with ZnO nanocrystals for antibacterial wound dressings
作者：Somia Yassin Hussain Abdalkarim, Hou-Yong Yu, Duanchao Wang, Juming Yao
關(guān)鍵字：Cellulose nanocrystal, Poly(3-hydroxybutyrate-co-3-hydroxyvalerate), Nanohybrids, Nanofibrous membranes, Wound dressings
論文來(lái)源：期刊
發(fā)表時(shí)間：2017年
Electrospinning was used to fabricate bioactive nanofibrous membranes from cellulose nanocrystal-ZnO (CNC-ZnO) nanohybrids as reinforcing materials in biodegradable poly(3-hydroxybutyrate-co-3-hydroxy-valerate) (PHBV) for potential use as wound dressings. Incorporation of CNC-ZnO considerably improved the uniformity and reduced the diameter of PHBV nanofibers with porosity in the range of 14–56%. Significant improvements in mechanical strength and thermal stability were achieved. Compared to neat PHBV, a 150% improvement in tensile strength and a 112.5% increase in Young’s modulus were obtained for the nanofibrous membranes with 5.0 wt% CNC-ZnO. Additionally, initial decomposition temperature (T0) and maximum decomposition temperature (Tmax) values were increased by 33.7 and 27.3 °C, respectively. It was also observed that CNC-ZnO had a positive effect on the barrier properties and absorbency of simulated fresh blood for nanofibrous membranes. Moreover, the nanofibrous membrane with 5.0 wt% had the highest absorbency (8.4 g/g) and exhibited the best antibacterial activity of about 100% against both E. coli and S. aureusbacteria. Hence, such nanofibrous membranes showed potential uses as antibacterial wound dressings.