High-flow nylon 6 by in situ polymerization: synthesis and characterization
作者:Fan Zhang, Li Zhou, Yaochi Liu, Weijian Xu, Yuanqin Xiong
關鍵字:high-flow,nylon
論文來源:期刊
具體來源:J Appl Polym Sci 2008, 108, 2365–2372.
發表時間:2008年
A new synthetic strategy for high flow nylon 6 was developed in this article. Generation 1, 2, 3 (G1, G2, G3) polyamidomine (PAMAM) dendrimers reacted with p-phthalic acid by equimolar terminal groups in water solution respectively,mother salt solution was then prepared. The high flow nylon 6 was prepared with suitable quantity of mother salt solution, end capping agent (acetic acid), and ε-caprolactam by in situ polymerization. Blue shifts are found for the peaks of NH(γN-H and  2δN-H ) of the high flow nylon 6 compared with pure nylon 6 in the IR spectra. Comparing with the pure nylon 6, the high flow nylon 6 comprises low content of PAMAM units, has high flow property and almost the same mechanical property. The Melt Flow Index (FMI) of the high flow nylon 6 increases (ca. 70-90%), and the tensile strength hardly decrease while the elongation at break decreases (ca. 20-35%). But the izod impact strength of the high flow nylon 6 increases. The SEM images show that the high flow nylon 6 presents brittle fracture with conglomeration-like structure while pure nylon 6 exhibits plastic fracture with island-like structure. DSC thermograms of non-isothermal crystallization exhibit that the peak of high flow nylon 6 broadens comparing with the pure nylon 6, the broader peak means the wider processing temperature.
主站蜘蛛池模板: 江安县| 同心县| 乌拉特中旗| 中阳县| 都昌县| 茶陵县| 石嘴山市| 吴川市| 墨竹工卡县| 社会| 高要市| 翼城县| 乐安县| 喀什市| 安乡县| 饶河县| 日土县| 常山县| 谢通门县| 德州市| 屯留县| 惠州市| 甘孜县| 荔波县| 时尚| 巴彦淖尔市| 仪陇县| 新宾| 彭水| 丹江口市| 隆尧县| 海丰县| 体育| 女性| 浦东新区| 本溪| 白朗县| 汨罗市| 高邮市| 金平| 龙里县|