Tribological behavior and morphology of PTFE particulate-reinforced POM matrix composites
作者：Qi Liu, Wei Luo, Shengtai Zhou, Huawei Zou*, Mei Liang*
關鍵字：polyoxymethylene (POM), polytetrafluoroethylene (PTFE), sliding speed, wear mechanism, weight average molar mass (Mw)
論文來源：期刊
具體來源：Journal of Polymer Engineering, 2017, 37(3): 227-237.
發表時間：2017年
Abstract: The friction and wear properties of polyoxymethylene/polytetrafluoroethylene (POM/PTFE) composites were investigated by using a block-on-ring friction tester and special focus was paid to the effect of weight average molar mass (Mw) of POM. To study the thermodynamic characteristics and wear mechanism of composites, differential scanning calorimetry (DSC) and scanning electron microscopy (SEM) were used. Results showed that friction and wear properties of the composite blends were strongly affected by the Mw of POM and the loading fractions of PTFE. POM/PTFE composites with lower Mw of POM owned better wear resistance abilities under a high-speed sliding regime, which resulted from the effective lubrication of transferred wear debris under a relatively high sliding speed. However, the transfer layer on the counterface could be easily peeled off under the low sliding speed,
resulting in higher wear rate of POM/PTFE composites with lower Mw of POM. POM and its composites with high Mw showed comparative high friction levels, related to the strong adhesion between the resin and the steel counterpart. DSC analysis showed that POM with lower Mw had higher crystallinity, which was beneficial to the improvement of wear resistance in a high-speed sliding condition.