| Surface modification of PBO fiber by coaxial atmospheric dielectric barrier discharge (PLA-PLA) |
| 關(guān)鍵詞： |
plasma treatment poly (1 4-phenylene-cis-benzobisoxazole) fibres atmospheric dielectric barrier di |
| 類(lèi) 別： |
纖維 >> 合成纖維 |
| 來(lái) 源： |
ICAFPM 2011 |
| 資料類(lèi)型： |
pdf文件 |
| 資料大小： |
3050K |
| 簡(jiǎn) 介： |
Surface modifications of poly (1, 4-phenylene-cis-benzobisoxazole) (PBO) fibres by coaxial atmospheric dielectric barrier discharge (PLA-PLA) have been studied in this paper. The mixture of argon and oxygen was used as inlet gas. The modification effects were examined by means of scanning electron microscopy (SEM), contact angle measurement (CA), the fourier transform infrared spectroscopy (FTIR) and the interlaminar shear strength (ILSS) measurement. The results indicated that the surface of treated PBO fibres became rougher compared to the untreated, and the contact angle decreased significantly by 25.03% from 84.7°to 63.5°after Ar/O2 plasma treatment for 3 minutes. The FTIR spectra showed that the polar functional groups were introduced into the surface of the PBO fibres after the treatment. Therefore, the interlaminar shear strength (ILSS) of PBO/D03E composite could be improved from 3.3 to 7.6 MPa. |
| 上傳人： |
epce |
| 上傳時(shí)間： |
2011-09-28 15:06:53 |
| 下載次數(shù)： |
1 |
| 消耗積分： |
4 |
| 我要收藏： |
 |
| |
友情提示：下載后對(duì)該資源進(jìn)行評(píng)論，即可獎(jiǎng)勵(lì)2分。 |
|
本欄目部分資源來(lái)自互聯(lián)網(wǎng)，僅為促進(jìn)數(shù)據(jù)共享和信息交流，如有版權(quán)問(wèn)題請(qǐng)告知本網(wǎng)或上傳者本人，本網(wǎng)會(huì)及時(shí)給予答復(fù)。 |
| 報(bào)告錯(cuò)誤
1.下載無(wú)效
2. 資料明顯無(wú)價(jià)值
3. 資料重復(fù)存在
|